Compoflex® SB 250

Compoflex® SB 250 is a peel ply, release film and breather, used to control flow rate and release consumables from a composite laminate. Compoflex® SB 250 generates a very rough and textured surface ideal for secondary bonding or painting of a composite laminate.

Compoflex® SB 250 may reduce or eliminate the need for sanding or abrading. Best results with epoxy resin, but we always recommend testing. Release film perforation style: low to medium bleed characteristics.

Compoflex® SB 250 is a medium weight breather (150g / 5 oz) ideal for low pressure cures and can be used as bleeder at any pressure. Works well with polyester, vinylester, epoxy, phenolic and other types of resin.

Technical data

PropertyCompoflex SB 250Standard
Recommended working temperature145°C (293°F) -
Fibre typePolypropylene-
Fabric constructionNonwoven-
Weight250 gsmEN 195
Thickness1.0 mmISO 9863 - 1
Tear resistance MD/CD305 N/195 NISO 9073 - 4
Pore size < 10 μmISO 12956

Notes

Working temperature
Recommended max. working temperature is 144°C (293°F). The melting point for polypropylene is 165°C (329°F). However, it is possible to use Compoflex® at 200°C (392°F) due to the fact that Compoflex® performs before the temperature exceeds the melting point. After cooling, the material becomes stable again, and peeling is just as easy as normal. We recommend conducting a test on a small part first.

Above technical data are indicative.
MD = Machine direction  
CD = Cross direction

Sizes
Width: 1.52 m (60 inch)
Length: 61 m (200 ft.)
Packing: 16 rolls per pallet each roll in clear foil 

Rolls can be cut to size maximum width available is 2.1 m (82.9 inch).